GE Engineering plastics Physical properties directory >> LEXAN™ PC >> EXL1330 Physical property table

[下載EXL1330物性表PDF] Consult EXL1330

Lexan PC EXL1330 Physical property

-60℃延展性,中等流動速率,UV穩定,不透明色.優異的加工性能,應用廣.

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	590	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	620	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	130	%	ASTM D 638
Tensile Modulus, 50 mm/min	21400	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	900	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	21000	kgf/cm2	ASTM D 790
Tensile Stress, yield, 50 mm/min	55	MPa	ISO 527
Tensile Stress, break, 50 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Tensile Modulus, 1 mm/min	2100	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
Flexural Modulus, 2 mm/min	2100	MPa	ISO 178
Hardness, H358/30	90	MPa	ISO 2039-1
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	81	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	69	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -50°C	59	cm-kgf/cm	ASTM D 256
Izod Impact, notched, 23°C, 6.4mm	65	cm-kgf/cm	ASTM D 256
Izod Impact, double-gated, 23°C	108	cm-kgf/cm	SABIC Method
Instrumented Impact Total Energy, 23°C	539	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m2	ISO 180/1U
Izod Impact, notched 80103 +23°C	70	kJ/m2	ISO 180/1A
Izod Impact, notched 80103 -30°C	55	kJ/m2	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	75	kJ/m2	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	60	kJ/m2	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	143	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	134	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	124	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.66E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.66E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	7.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.2E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	143	°C	ISO 306
Vicat Softening Temp, Rate B/120	145	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	136	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	125	°C	ISO 75/Ae
Relative Temp Index, Elec	125	°C	UL 746B
Relative Temp Index, Mech w/impact	115	°C	UL 746B
Relative Temp Index, Mech w/o impact	120	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.18	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	10	g/10 min	ASTM D 1238
Density	1.18	g/cm2	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm210 min	ISO 1133
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	0.8	mm	UL 94
Glow Wire Flammability Index 850°C, passes at	0.8	mm	IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	875	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	875	°C	IEC 60695-2-13
Oxygen Index (LOI)	35	%	ISO 4589

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	215 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

Parameter
Sheet Extrusion	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	245 - 260	°C
Barrel - Zone 1 Temperature	250 - 290	°C
Barrel - Zone 2 Temperature	245 - 270	°C
Barrel - Zone 3 Temperature	225 - 255	°C
Adapter Temperature	225 - 255	°C
Die Temperature	240 - 260	°C
Roll Stack Temp - Top	75 - 115	°C
Roll Stack Temp - Middle	80 - 125	°C
Roll Stack Temp - Bottom	120 - 145	°C

[下載EXL1330物性表PDF] Consult EXL1330

Physical properties of related products: 1173X BX9349 EX7631T EXL9330 EXL9132 EXL9134 EXL9335 EXL1414 EXL4419 EXL1414H EXL1132 ML7667 EXL1413T ML6413 ML6411 ML6412 EXL1494T EXL1463T EXL1433T EXL1414T EXL1443T EXL1434T EXL1434 EXL6414 EXL9112 EXL5689 EXL1162T EXL1132T EXL1810T EXL4016H EXL1192C EXL8414 EXL1483T EXL1484T EXL1036 EXL1493T EXL1182T EXL1890T EXL1112T EXL1112 EXL8134 EXL8454 EXL8483 EXL9330S EX1632T

Correlation search: EXL1330-111 EXL1330-701 EXL1330-BK1066 EXL1330-NA Lexan EXL1330 EXL1330物性 Sabic EXL1330 GE EXL1330 PC EXL1330 PC 工程塑料聚碳酸酯 PC 塑料 PC 物性

廣州華秀塑膠有限公司不僅是專業的Lexan PC EXL1330原料供應商，亦注重技術支持及全方位的解決方案，提供從材料鑒定、模具設計、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之Lexan PC EXL1330材料，進而協助客戶提高產品竟爭力。

聯絡我們

地址:廣州市天河區中山大道中439號東圃天銀商貿大廈1720-1723室

電話:020-82582555

傳真:020-82523699

Email: sales@va-so.cn

Lexan PC EXL1330報價 >>

常規產品

長纖增強尼龍66 長纖增強PPA
長纖增強尼龍6 長纖增強PP
長纖增強復合材料沖擊改性復合尼龍66
沖擊改性復合尼龍6 高強尼龍
沖擊改性復合尼龍沖擊改性復合材料
改性PP 改性的合金料
高溫改性塑料含氟聚合物
改性POM 改性PBT
改性PC 焊接用復合塑料
高比重復合塑料永久防靜電塑料
永久防靜電ABS 永久防靜電合金
永久防靜電POM 其他導電材料
導電尼龍導電PE,導電PP
高溫導電塑料導電POM
導電PBT 導電PC
其他非PTFE自潤滑塑料非PTFE自潤滑PA
非PTFE自潤滑聚苯醚非PTFE自潤滑PPA
非PTFE自潤滑聚甲醛非PTFE自潤滑聚碳酸酯
其他潤滑塑料潤滑尼龍
潤滑烯烴潤滑PPO(PPE+PS)
耐熱潤滑塑料潤滑POM
潤滑PBT 潤滑彈性體
潤滑PC 擠出PBT
熱傳導復合塑料其他PC
EMI/RFI屏蔽復合塑料預著色非填充樹脂