GE Engineering plastics Physical properties directory >> LEXAN™ PC >> EXL9112 Physical property table

[下載EXL9112物性表PDF] Consult EXL9112

Lexan PC EXL9112 Physical property

-20℃延展性,耐燃性 V-0/5VA. 非鹵化,不含溴.

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	590	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	590	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	5.8	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	103	%	ASTM D 638
Tensile Modulus, 50 mm/min	23100	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	970	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	23800	kgf/cm2	ASTM D 790
Tensile Stress, yield, 50 mm/min	59	MPa	ISO 527
Tensile Stress, break, 50 mm/min	55	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	100	%	ISO 527
Tensile Modulus, 1 mm/min	2200	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	88	MPa	ISO 178
Flexural Modulus, 2 mm/min	2300	MPa	ISO 178
Hardness, H358/30	95	MPa	ISO 2039-1
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	74	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	57	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy, 23°C	692	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m2	ISO 180/1U
Izod Impact, notched 80103 +23°C	55	kJ/m2	ISO 180/1A
Izod Impact, notched 80103 -30°C	20	kJ/m2	ISO 180/1A
Izod Impact, notched 80104 +23°C	53	kJ/m2	ISO 180/1A
Izod Impact, notched 80104 -30°C	18	kJ/m2	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	60	kJ/m2	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	25	kJ/m2	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	143	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	136	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	123	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.2E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.2E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	7.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.5E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	143	°C	ISO 306
Vicat Softening Temp, Rate B/120	144	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	136	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	124	°C	ISO 75/Ae
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.18	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	17	g/10 min	ASTM D 1238
Density	1.19	g/cm2	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	16	cm210 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Dielectric Strength, in oil, 3.2 mm	19	kV/mm	IEC 60243-1
Relative Permittivity, 50/60 Hz	2.7	-	IEC 60250
Relative Permittivity, 1 MHz	2.7	-	IEC 60250
Dissipation Factor, 50/60 Hz	0	-	IEC 60250
Dissipation Factor, 1 MHz	0.01	-	IEC 60250
Comparative Tracking Index	175	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	1.52	mm	UL 94
UL Recognized, 94-5VA Rating (3)	3.04	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	825	°C	IEC 60695-2-13
Oxygen Index (LOI)	40	%	ISO 4589
UV-light, water exposure/immersion	f1	-	UL 746C

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	215 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

[下載EXL9112物性表PDF] Consult EXL9112

Physical properties of related products: 1173X BX9349 EX7631T EXL1330 EXL9330 EXL9132 EXL9134 EXL9335 EXL1414 EXL4419 EXL1414H EXL1132 ML7667 EXL1413T ML6413 ML6411 ML6412 EXL1494T EXL1463T EXL1433T EXL1414T EXL1443T EXL1434T EXL1434 EXL6414 EXL5689 EXL1162T EXL1132T EXL1810T EXL4016H EXL1192C EXL8414 EXL1483T EXL1484T EXL1036 EXL1493T EXL1182T EXL1890T EXL1112T EXL1112 EXL8134 EXL8454 EXL8483 EXL9330S EX1632T

Correlation search: EXL9112-111 EXL9112-701 EXL9112-BK1066 EXL9112-NA Lexan EXL9112 EXL9112物性 Sabic EXL9112 GE EXL9112 PC EXL9112 Sabic PC 聚碳酸酯 PC 工程塑料 PC 物性

廣州華秀塑膠有限公司不僅是專業的Lexan PC EXL9112原料供應商，亦注重技術支持及全方位的解決方案，提供從材料鑒定、模具設計、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之Lexan PC EXL9112材料，進而協助客戶提高產品竟爭力。

聯絡我們

地址:廣州市天河區中山大道中439號東圃天銀商貿大廈1720-1723室

電話:020-82582555

傳真:020-82523699

Email: sales@va-so.cn

Lexan PC EXL9112報價 >>

常規產品

長纖增強尼龍66 長纖增強PPA
長纖增強尼龍6 長纖增強PP
長纖增強復合材料沖擊改性復合尼龍66
沖擊改性復合尼龍6 高強尼龍
沖擊改性復合尼龍沖擊改性復合材料
改性PP 改性的合金料
高溫改性塑料含氟聚合物
改性POM 改性PBT
改性PC 焊接用復合塑料
高比重復合塑料永久防靜電塑料
永久防靜電ABS 永久防靜電合金
永久防靜電POM 其他導電材料
導電尼龍導電PE,導電PP
高溫導電塑料導電POM
導電PBT 導電PC
其他非PTFE自潤滑塑料非PTFE自潤滑PA
非PTFE自潤滑聚苯醚非PTFE自潤滑PPA
非PTFE自潤滑聚甲醛非PTFE自潤滑聚碳酸酯
其他潤滑塑料潤滑尼龍
潤滑烯烴潤滑PPO(PPE+PS)
耐熱潤滑塑料潤滑POM
潤滑PBT 潤滑彈性體
潤滑PC 擠出PBT
熱傳導復合塑料其他PC
EMI/RFI屏蔽復合塑料預著色非填充樹脂